FerriticEN 1.4016 · UNS S43000
Stainless Steel AISI 430 | Complete Technical Data Sheet
AISI 430 (EN 1.4016) is the world's most widely used ferritic grade. With 16–18% chromium, it offers good oxidation and atmospheric corrosion resistance, without nickel, at significantly lower cost than 304. It is magnetic and cannot be hardened by heat treatment.
Density7.74 g/cm³
Melting Range1425–1510 °C
Rm (MPa)≥450
Rp0.2 (MPa)≥205
Chemical Composition
| C | Si | Mn | P | S | Cr | Ni |
|---|---|---|---|---|---|---|
| ≤0.12 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.030 | 16.0–18.0 | ≤0.75 |
Values in % mass. Source: ASTM A240 / EN 10088.
Mechanical Properties
| Property | Value | Unit |
|---|---|---|
| Tensile Strength (Rm) | ≥450 | MPa |
| Yield Strength (Rp0.2) | ≥205 | MPa |
| Elongation (A) | ≥22 | % |
| Brinell Hardness (HB) | ≤183 | HB |
Minimum values in annealed condition per ASTM A240 / EN 10088-2.
International Equivalences
| ASTM | EN (DIN) | UNS | JIS | GB |
|---|---|---|---|---|
| A240 Type 430 | 1.4016 | S43000 | SUS430 | 10Cr17 |
Main Applications
Appliances (dishwashers, washing machines)
Professional kitchen equipment
Interior decorative finishes
Facade panels
Heating equipment
Automotive exhaust (cold zone)
Sinks and kitchen equipment
Frequently Asked Questions
Related Grades
Quote
Quote 430
Response within 24h for qualified requests.
MTC available
ISO 9001
Physical Properties
- Density
- 7.74 g/cm³
- Melting range
- 1425–1510 °C
- Family
- Ferritic
- Magnetic?
- Yes